Molding Properties
· Drying temperature : 85°C
· Drying time : 2~4hr
· Injection forming cylinder temperature : 200~260°C
· Injection molding tool temperature : 50~80°C
· Injection molding pressure : 1050~2810kgf/cm2
· Compression molding temperature : —
· Compression molding pressure : —
· Molding shrinkage rate : 0.1~0.2%
· Specific gravity : 1.20~1.46density
JIS : K6911,K7122
A.S.T.M : D792
Mechanical Characteristics
· Tensile strength : 600~1410kgf/cm2
JIS : K6911,K7113
A.S.T.M : D638
· Tensile elongation : 1.1~3.8%
· Compressive strength : 1550kgf/cm2
JIS : K7208
· Flexure strength : 1550~1830kgf/cm2
JIS : K7203
· Izot impact strength : —
JIS : K7110,K7111
· Rockwell hardness : M100 • E60
JIS : K7202
A.S.T.M : D785
Thermal Characteristic
· Heat resistance temperature (continuous) : 93~104°C
· Deflection temperature under load
a) Bending stress18.6kgf/cm2 : 88~110°C
b) Bending stress 4.6kgf/cm2 : 101~115°C
JIS : K7206,K7207
A.S.T.M : D648
Acrylonitrile-Styrene
SAN General
· Drying temperature : 85°C
· Drying time : 2~4hr
· Injection forming cylinder temperature : 200~260°C
· Injection molding tool temperature : 50~80°C
· Injection molding pressure : 1050~2810kgf/cm2
· Compression molding temperature : —
· Compression molding pressure : —
· Molding shrinkage rate : 0.1~0.2%
· Specific gravity : 1.20~1.46density
JIS : K6911,K7122
A.S.T.M : D792
Mechanical Characteristics
· Tensile strength : 600~1410kgf/cm2
JIS : K6911,K7113
A.S.T.M : D638
· Tensile elongation : 1.1~3.8%
· Compressive strength : 1550kgf/cm2
JIS : K7208
· Flexure strength : 1550~1830kgf/cm2
JIS : K7203
· Izot impact strength : —
JIS : K7110,K7111
· Rockwell hardness : M100 • E60
JIS : K7202
A.S.T.M : D785
Thermal Characteristic
· Heat resistance temperature (continuous) : 93~104°C
· Deflection temperature under load
a) Bending stress18.6kgf/cm2 : 88~110°C
b) Bending stress 4.6kgf/cm2 : 101~115°C
JIS : K7206,K7207
A.S.T.M : D648