SAN general

Molding Properties
   ·   Drying temperature                                   : 85°C
   ·   Drying time                                               : 2~4hr
   ·   Injection forming cylinder temperature       : 200~260°C
   ·   Injection molding tool temperature             : 50~80°C
   ·   Injection molding pressure                         : 710~2320kgf/cm­­2
   ·   Compression molding temperature             : 150~200°C
   ·   Compression molding pressure                   : 70.3~703kgf/cm2
   ·   Molding shrinkage rate                               : 0.2~0.7%
   ·   Specific gravity                                          : 1.07~1.10density
     JIS            : K6911,K7122
     A.S.T.M   : D792


Mechanical Characteristics
   ·   Tensile strength                           : 600~840kgf/cm2
     JIS : K6911,K7113
     A.S.T.M   : D638
   ·   Tensile elongation                       : 1.5~3.7%
   ·   Compressive strength                 : 984~1200kgf/cm2
     JIS : K7208
   ·   Flexure strength                          : 984~1340kgf/cm2
     JIS : K7203
   ·   Izot impact strength                    : —
     JIS : K7110,K7111
   ·   Rockwell hardness                     : M80~90
     JIS : K7202
     A.S.T.M   : D785


Thermal Characteristic
   ·   Heat resistance temperature (continuous)   : 60~96°C
   ·   Deflection temperature under load
       a) Bending stress18.6kgf/cm2                   : 88~104°C
       b) Bending stress 4.6kgf/cm2                    : —
     JIS            : K7206,K7207
     A.S.T.M   : D648




Acrylonitrile-Styrene
SAN-GF Glass fiber 20~30%