Nylon 66-PA66 Glass Fiber 30%


Molding properties
    ·      Drying temperature                                  : 80°C
    ·      Drying time                                              : 8~15hr
    ·      Injection forming cylinder temperature      : 260~300°C
    ·      Injection molding tool temperature            : 40~120°C
    ·      Injection molding pressure                        : —
    ·      Compression molding temperature            : —
    ·      Compression molding pressure                 : —
    ·      Molding shrinkage rate                             : 0.5%
    ·      Specific gravity                                        : 1.38density
      JIS : K6911,K7122
      A.S.T.M   : D792


Mechanical characteristics
    ·    Tensile strength                  : 1850kgf/cm2
      JIS : K6911,K7113
      A.S.T.M   : D638
    ·    Tensile elongation               : 3%
    ·    Compressive strength         : 2070kgf/cm2
      JIS : K7208
    ·    Flexure strength                  : 471~1260kgf/cm2
      JIS : K7203
    ·     Izot impact strength           : 12kgf/cm2
      JIS : K7110,K7111
    ·     Rockwell hardness            : M100
      JIS : K7202
           A.S.T.M   : D785


Thermal characteristic
    ·    Heat resistance temperature (continuous)   : 82~121°C
    ·    Deflection temperature under load
         a) Bending stress18.6kgf/cm2                    : 77.0°C
         b) Bending stress 4.6kgf/cm2                     : 236~239°C
           JIS            : K7206,K7207
           A.S.T.M   : D648