Polycarbonate General

Molding Properties
  ·    Drying temperature                                 : 120°C
  ·    Drying time                                             : >4hr
  ·    Injection forming cylinder temperature     : 270~380°C
  ·    Injection molding tool temperature           : 80~120°C
  ·    Injection molding pressure                       : 700~1410kgf/cm­­2
  ·    Compression molding temperature           : 249~326°C
  ·    Compression molding pressure                 : 0.70~1.41kgf/cm2
  ·    Molding shrinkage rate                             : 0.5~0.7%
  ·    Specific gravity                                        : 1.19~1.20density
     JIS : K6911,K7122
     A.S.T.M   : D792


Mechanical Characteristics
  ·    Tensile strength                      : 550~700kgf/cm2
     JIS : K6911,K7113
     A.S.T.M   : D638
  ·    Tensile elongation                   : 100~130%
  ·    Compressive strength                 : 844kgf/cm2
     JIS : K7208
  ·    Flexure strength                      : 949kgf/cm2
     JIS : K7203
  ·    Izot impact strength                : 75~100kgf/cm2
     JIS : K7110,K7111
  ·    Rockwell hardness                 : R115~125
     JIS : K7202
     A.S.T.M   : D785


Thermal Characteristic
  ·    Heat resistance temperature (continuous)    : 121°C
  ·    Deflection temperature under load
       a)  Bending stress18.6kgf/cm2                    : 129~140°C
       b)  Bending stress 4.6kgf/cm2                     : 132~143°C
     JIS            : K7206,K7207
     A.S.T.M   : D648


Polycarbonate
PC-GF glass fiber 10% or less
PC GF Glass fiber 10~40%