Silicone


Application:

Electric parts
Lubricants

SI Glass fiber

Molding properties

Drying temperature                                          : —
Drying time                                                      : —
Injection forming cylinder temperature              : —
Injection molding tool temperature                    : —
Injection molding pressure                                : —
Compression molding temperature                    : 154~182°C
Compression molding pressure                         : 70.3~350kgf/cm2
Molding shrinkage rate                                     : 0~0.5%
Specific gravity                                                 : 1.80~1.94density
                JIS            : K6911,K7122
                A.S.T.M   : D792

Mechanical characteristics

Tensile strength                                               : 281~457kgf/cm2
               JIS            : K6911,K7113
              A.S.T.M   : D638
Tensile elongation                                           : —
Compressive strength                                     : 103~1050kgf/cm2
               JIS            : K7208
Flexure strength                                              : 703~984kgf/cm2
              JIS            : K7203
Izot impact strength                                        : 1.63~43.5kgf/cm2
             JIS            : K7110,K7111
Rockwell hardness                                          : M80~90
            JIS            : K7202
            A.S.T.M   : D785

Thermal characteristic

Heat resistance temperature (continuous)   : >315°C
Deflection temperature under load
         a) Bending stress18.6kgf/cm2               : >482°C
         b) Bending stress 4.6kgf/cm2                : —
                 JIS            : K7206,K7207
                 A.S.T.M   : D648

Urea-formaldehyde


Application:

Laminated sheets
Textile
Colorant
Knobs
Tableware


Molding properties

Drying temperature                                           : —
Drying time                                                       : —
Injection forming cylinder temperature                : 143~160°C
Injection molding tool temperature                     : —
Injection molding pressure                                 : 1050~1410kgf/cm¬¬2
Compression molding temperature                     : 135~176°C
Compression molding pressure                          : 141~562kgf/cm2
Molding shrinkage rate                                      : 0.6~1.4%
Specific gravity                                                 : 1.47~1.52density
        JIS            : K6911,K7122
        A.S.T.M   : D792

Mechanical characteristics

Tensile strength                                              : 387~914kgf/cm2
                JIS            : K6911,K7113
                A.S.T.M   : D638
Tensile elongation                                           : 0.5~1.0%
Compressive strength                                     : 176~316kgf/cm2
               JIS            : K7208
Flexure strength                                              : 703~1270kgf/cm2
              JIS            : K7203
Izot impact strength                                        : 1.36~2.18kgf/cm2
              JIS            : K7110,K7111
Rockwell hardness                                          : M10~120
              JIS            : K7202
              A.S.T.M   : D785

Thermal characteristic

Heat resistance temperature (continuous)          : 76.5°C
Deflection temperature under load
        a) Bending stress18.6kgf/cm2                       : 126~143°C
        b) Bending stress 4.6kgf/cm2                        : —
               JIS            : K7206,K7207
               A.S.T.M   : D648