Unsaturated polyester Glass fiber SMC

Molding Properties
          ·         Drying temperature                               : —
          ·         Drying time                                           : —
          ·         Injection forming cylinder temperature   : —
          ·         Injection molding tool temperature         : —
          ·         Injection molding pressure                     : —
          ·         Compression molding temperature         : 132~176°C
          ·         Compression molding pressure              : 21.1~94.4kgf/cm2
          ·         Molding shrinkage rate                          : 0.1~0.4%
          ·         Specific gravity                                      : 1.65~2.60density
               JIS            : K6911,K7122
               A.S.T.M   : D792


Mechanical Characteristics
           ·         Tensile strength                                        : 562~1410kgf/cm2
             JIS            : K6911,K7113
             A.S.T.M   : D638
           ·         Tensile elongation                                    : 3%
           ·         Compressive strength                              : 1050~2110kgf/cm2
             JIS            : K7208
           ·         Flexure strength                                      : 703~2530kgf/cm2
            JIS            : K7203
           ·         Izot impact strength                                 : 38.1~120kgf/cm2
            JIS            : K7110,K7111
           ·         Rockwell hardness                                  : barcol 50~70
            JIS            : K7202
            A.S.T.M   : D785


Thermal Characteristic
            ·         Heat resistance temperature (continuous)   : 149~204°C
            ·         Deflection temperature under load
                      a)      Bending stress18.6kgf/cm2               : 190~260°C
                      b)      Bending stress 4.6kgf/cm2                : —
              JIS            : K7206,K7207
              A.S.T.M   : D648

Unsaturated polyester Glass fiber Roving
Unsaturated polyester Glass fiber Premix

Unsaturated Polyester Glass fiber Premix

Molding Properties
            ·         Drying temperature                                     : —
            ·         Drying time                                                 : —
            ·         Injection forming cylinder temperature         : —
            ·         Injection molding tool temperature               : —
            ·         Injection molding pressure                           : —
            ·         Compression molding temperature               : 138~176°C
            ·         Compression molding pressure                    : 35.2~141kgf/cm2
            ·         Molding shrinkage rate                                : 0.1~1.2%
            ·         Specific gravity                                            : 1.65~2.30density
                 JIS            : K6911,K7122
                A.S.T.M   : D792


Mechanical Characteristics
            ·         Tensile strength                                      : 211~703kgf/cm2
               JIS            : K6911,K7113
               A.S.T.M   : D638
            ·         Tensile elongation                                   : 0.5~2.0%
            ·         Compressive strength                             : 1410~2110kgf/cm2
               JIS            : K7208
            ·         Flexure strength                                      : 492~1410kgf/cm2
               JIS            : K7203
            ·         Izot impact strength                                 : 8.16~87.1kgf/cm2
               JIS            : K7110,K7111
            ·         Rockwell hardness                                  : barcol 50~80
               JIS            : K7202
               A.S.T.M   : D785


Thermal Characteristic
             ·         Heat resistance temperature (continuous)   : 149~176°C
             ·         Deflection temperature under load
                       a)      Bending stress18.6kgf/cm2               : >204°C
                       b)      Bending stress 4.6kgf/cm2                : —
                JIS            : K7206,K7207
                A.S.T.M   : D648

Unsaturated Polyester Glass fiber Roving
Unsaturated Polyester Glass fiber SMC

Unsaturated Polyester

Applications:

          ·         TV tuners
          ·         Fuses
          ·         Breakers
          ·         Motor covers
          ·         Power distributor case covers
          ·         Press rings
          ·         Rectifier frames

Unsaturated Polyester Glass roving

Molding Properties

          ·         Drying temperature                                        : —
          ·         Drying time                                                    : —
          ·         Injection forming cylinder temperature            : —
          ·         Injection molding tool temperature                  : —
          ·         Injection molding pressure                              : —
          ·         Compression molding temperature                  : 76.5~160°C
          ·         Compression molding pressure                       : 17.6~141kgf/cm2
          ·         Molding shrinkage rate                                   : 0.02~0.2%
          ·         Specific gravity                                               : 1.35~2.30density
              JIS            : K6911,K7122
              A.S.T.M   : D792

Mechanical Characteristics

          ·         Tensile strength                                        : 1050~2110kgf/cm2
             JIS            : K6911,K7113
             A.S.T.M   : D638
          ·         Tensile elongation                                    : 0.5~5.0%
          ·         Compressive strength                              : 1050~2110kgf/cm2
             JIS            : K7208
          ·         Flexure strength                                       : 703~1270kgf/cm2
             JIS            : K7203
          ·         Izot impact strength                                 : 10.9~109kgf/cm2
             JIS            : K7110,K7111
          ·         Rockwell hardness                                  : barcol 50~80
             JIS            : K7202
             A.S.T.M   : D785

Thermal Characteristic

           ·         Heat resistance temperature (continuous)       : 149~176°C
           ·         Deflection temperature under load
                     a)      Bending stress18.6kgf/cm2                   : >204°C
                     b)      Bending stress 4.6kgf/cm2                    : —
             JIS            : K7206,K7207
             A.S.T.M   : D648

 

Unsaturated Polyester Glass Premix

Unsaturated Polyester Glass SMC

Liquid Crystal Polymer-GF glass fiber 40%

Molding Properties
        ·         Drying temperature                                  : 140~160°C
        ·         Drying time                                                       : 4hr
        ·         Injection forming cylinder temperature      : 290~310°C
        ·         Injection molding tool temperature            : 70~110°C
        ·         Injection molding pressure                        : 400~900kgf/cm­­2
        ·         Compression molding temperature            : —
        ·         Compression molding pressure                 : —
        ·         Molding shrinkage rate                             : Flow direction 0.1~0.15
                                                                                   Traverse direction 0.3~0.5
        ·         Specific gravity                                         : 1.70density
            JIS            : K6911,K7122
            A.S.T.M   : D792


Mechanical Characteristics
         ·         Tensile strength                                        : 900kgf/cm2
            JIS            : K6911,K7113
            A.S.T.M   : D638
         ·         Tensile elongation                                     : 1.8%
         ·         Compressive strength                               : —
            JIS            : K7208
         ·         Flexure strength                                        : —
           JIS            : K7203
         ·         Izot impact strength                                  : 8.7kgf/cm2
           JIS            : K7110,K7111
         ·         Rockwell hardness                                   : R79
           JIS            : K7202
           A.S.T.M   : D785


Thermal Characteristic
          ·         Heat resistance temperature (continuous)        : —
          ·         Deflection temperature under load
                    a)      Bending stress18.6kgf/cm2                    : 319°C
                    b)      Bending stress 4.6kgf/cm2                     :
           JIS            : K7206,K7207
           A.S.T.M   : D648

Liquid Crystal Polymer

Liquid Crystal Polymer

Application:
       ·         Connectors
       ·         Electronic parts

Molding Properties
       ·         Drying temperature                                 : 140~160°C
       ·         Drying time                                             : 4hr
       ·         Injection forming cylinder temperature     : 360~390°C
       ·         Injection molding tool temperature           : 70~110°C
       ·         Injection molding pressure                       : 400~900kgf/cm­­2
       ·         Compression molding temperature           : —
       ·         Compression molding pressure                : —
       ·         Molding shrinkage rate                            : Flow direction 0.1~0.2
                                                                                 Traverse direction 0.6~0.9
       ·         Specific gravity                                       : 1.35density
   JIS            : K6911,K7122
   A.S.T.M   : D792

Mechanical Characteristics
       ·         Tensile strength                                         : 1060~1335kgf/cm2
               JIS            : K6911,K7113
               A.S.T.M   : D638
       ·         Tensile elongation                                      : 1.3~4.5%
       ·         Compressive strength                                : —
               JIS            : K7208
       ·         Flexure strength                                         : —
               JIS            : K7203
       ·         Izot impact strength                                   : 13~21kgf/cm2
               JIS            : K7110,K7111
       ·         Rockwell hardness                                    : R60~63
               JIS            : K7202
               A.S.T.M   : D785

Thermal Characteristic
        ·         Heat resistance temperature (continuous)      : —
        ·         Deflection temperature under load
                  a)      Bending stress18.6kgf/cm2                  : 337~225°C
                  b)      Bending stress 4.6kgf/cm2                   :
             JIS            : K7206,K7207
             A.S.T.M   : D648

  

Liquid Crystal Polymer-GF glass fiber 40%