Phenol-Formaldehyde Glass fiber High strength

Molding Properties
       ·         Drying temperature                                           : —
       ·         Drying time                                                       : —
       ·         Injection forming cylinder temperature               : 165~199°C
       ·         Injection molding tool temperature                     : —
       ·         Injection molding pressure                                 : 352~1410kgf/cm­­2
       ·         Compression molding temperature                     : 149~193°C
       ·         Compression molding pressure                          : 70.3~422kgf/cm2
       ·         Molding shrinkage rate                                      : 0.1~0.4%
       ·         Specific gravity                                                  : 1.69~2.0density
            JIS            : K6911,K7122
            A.S.T.M   : D792


Mechanical Characteristics
        ·         Tensile strength                                               : 352~1270kgf/cm2
               JIS            : K6911,K7113
               A.S.T.M   : D638
        ·         Tensile elongation                                            : 0.2%
        ·         Compressive strength                                      : 1120~4920kgf/cm2
               JIS            : K7208
        ·         Flexure strength                                               : 703~4220kgf/cm2
               JIS            : K7203
        ·         Izot impact strength                                         : 1.63~100kgf/cm2
               JIS            : K7110,K7111
        ·         Rockwell hardness                                          : E54~101
               JIS            : K7202
               A.S.T.M   : D785


Thermal Characteristic
         ·         Heat resistance temperature (continuous)        : 176~288°C
         ·         Deflection temperature under load
                   a)      Bending stress18.6kgf/cm2                   : 149~315°C
                   b)      Bending stress 4.6kgf/cm2                    : —
              JIS            : K7206,K7207
              A.S.T.M   : D648





Phenol-Formaldehyde
Phenol-Formaldehyde Wood flour, cotton high impact proof

Phenol-Formaldehyde Wood flour, cotton high impact proof

Molding Properties
      ·         Drying temperature                                           : —
      ·         Drying time                                                       : —
      ·         Injection forming cylinder temperature               : 183~222°C
      ·         Injection molding tool temperature                     : —
      ·         Injection molding pressure                                 : 703~1410kgf/cm­­2
      ·         Compression molding temperature                     : 143~193°C
      ·         Compression molding pressure                          : 123~334kgf/cm2
      ·         Molding shrinkage rate                                      : 0.4~0.9%
      ·         Specific gravity                                                  : 1.34~1.45density
         JIS            : K6911,K7122
         A.S.T.M   : D792


Mechanical Characteristics
       ·         Tensile strength                                              : 352~633kgf/cm2
                JIS            : K6911,K7113
                A.S.T.M   : D638
       ·         Tensile elongation                                          : 0.4~0.8%
       ·         Compressive strength                                    : 155~253kgf/cm2
                JIS            : K7208
       ·         Flexure strength                                             : 492~984kgf/cm2
                JIS            : K7203
       ·         Izot impact strength                                        : 1.31~3.27kgf/cm2
                JIS            : K7110,K7111
       ·         Rockwell hardness                                         : M100~115
                JIS            : K7202
                A.S.T.M   : D785


Thermal Characteristic
        ·         Heat resistance temperature (continuous)     : 149~176°C
        ·         Deflection temperature under load
                  a)      Bending stress18.6kgf/cm2                 : 149~188°C
                  b)      Bending stress 4.6kgf/cm2                  : —
            JIS            : K7206,K7207
            A.S.T.M   : D648





Phenol-Formaldehyde
Phenol-Formaldehyde  Glass fiber High strength

Phenol-formaldehyde

Application:
         ·         Connectors
         ·         Switches
         ·         Tuners
         ·         Breakers
         ·         Coils
         ·         Bobbins

Phenol-formaldehyde( PF)


 Molding Properties
                ·         Drying temperature                                       : —
                ·         Drying time                                                   : —
                ·         Injection forming cylinder temperature           : —
                ·         Injection molding tool temperature                : —
                ·         Injection molding pressure                            : —
                ·         Compression molding temperature                : 132~160°C
                ·         Compression molding pressure                     : 123~263kgf/cm2
                ·         Molding shrinkage rate                                 : 1.0~1.2%
                ·         Specific gravity                                             : 1.21~1.30density
          JIS            : K6911,K7122
          A.S.T.M   : D792

Mechanical Characteristics
                 ·         Tensile strength                                              : 492~562kgf/cm2
                      JIS            : K6911,K7113
                      A.S.T.M   : D638
                 ·         Tensile elongation                                           : 1.0~1.5%
                 ·         Compressive strength                                     : 703~2190kgf/cm2
                     JIS            : K7208
                 ·         Flexure strength                                              : 844~1050kgf/cm2
                      JIS            : K7203
                 ·         Izot impact strength                                         : 10.9~1.96kgf/cm2
                      JIS            : K7110,K7111
                 ·         Rockwell hardness                                          : M124~128
                      JIS            : K7202
                      A.S.T.M   : D785

Thermal Characteristic
                 ·         Heat resistance temperature (continuous)     : 121°C
                 ·         Deflection temperature under load(°C)
                           a)      Bending stress18.6kgf/cm2                 : 115~126°C
                          b)      Bending stress 4.6kgf/cm2                   : —
                    JIS            : K7206,K7207
                    A.S.T.M   : D648

Phenol-Formaldehyde Wood flour, cotton high impact proof

Phenol-Formaldehyde  Glass fiber High strength

Melamine Formaldehyde

Application:
         ·         Push buttons
         ·         Handles
         ·         Knobs
         ·         Arc extinguishing panels
         ·         Tableware

Molding Properties
         ·         Drying temperature                                           : —
         ·         Drying time                                                       : —
         ·         Injection forming cylinder temperature               : 143~171°C
         ·         Injection molding tool temperature                    : —
         ·         Injection molding pressure                                : 1050~1410kgf/cm2
         ·         Compression molding temperature                    : 138~188°C
         ·         Compression molding pressure                         : 105~562kgf/cm2
         ·         Molding shrinkage rate                                     : 0.5~1.5%
         ·         Specific gravity                                                 : 1.47~1.52density
                JIS            : K6911,K7122
                A.S.T.M   : D792

Mechanical Characteristics
         ·         Tensile strength                                               : 492~914kgf/cm2
            JIS            : K6911,K7113
            A.S.T.M   : D638
         ·         Tensile elongation                                           : 0.6~0.9%
         ·         Compressive strength                                     : 2810~3160kgf/cm2
            JIS            : K7208
          ·         Flexure strength                                             : 703~1120kgf/cm2
            JIS            : K7203
          ·         Izot impact strength                                       : 1.31~1.91kgf/cm2
            JIS            : K7110,K7111
          ·         Rockwell hardness                                        : M115~125
            JIS            : K7202
            A.S.T.M   : D785

Thermal Characteristic

          ·         Heat resistance temperature (continuous)                : 99°C
          ·         Deflection temperature under load   (°C )        
                    a)      Bending stress               18.6kgf/cm2            : 176°C-188°C
                    b)      Bending stress               4.6kgf/cm2              : -
            JIS            : K7206,K7207
            A.S.T.M   : D648